Grinding Finishing Hot Rolled 17-4PH Stainless Steel Bar in 6m Length

証明	ISO, AISI, ASTM, EN, DIN, JIS
最小注文数量	50 kg
価格	US $3.19-3.68 / kg

商品の詳細

形	ラウンド	技術	熱間圧延
表面処理	明るい	直径範囲	8～450mm
長さ	6m	材質グレード	17-4ph
抗張力	1105～1310MPa	降伏強さ	1000～1170MPa
伸長	10-16%	硬度	28-44HRC
密度	7750kg/m3	熱伝導率	18.4-22.7W/mK
電気抵抗率	800nΩ・m	熱処理温度	1040℃
老化する温度	482～621℃
ハイライト	Grinding Finishing Stainless Steel Bar , 6m Length 17-4PH Stainless Steel Bar , Hot Rolled Round Bar

メッセージ

製品の説明

Grinding Finishing Stainless Steel Bar Grade 17-4PH Stainless Bar in 6m Length

High-strength precipitation hardening stainless steel bars with excellent corrosion resistance and mechanical properties.

Product Specifications

Products	17-4PH Stainless Steel Round Bar
Standard	ASTM GB DIN EN
Diameter	8 - 450mm
Length	6m /pcs or cutting as request
Finishing	black bar / Bright Bar
Main Grades	201 301 303Cu 304 304L 309S 310S 316L 316Ti 317L 318 321 347 410 420 430 431 440a/b/c 904L 2205 2507 Hastelloy C276 C4 C22 Inconel 600 625 Incoloy 800 825 825H etc
Service	Cutting, surface polishing, heat treatment
Brand	Walsin BAOSTEEL TISCO QINGSHAN

Material Description

17-4 Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and moderate corrosion resistance. High strength is maintained to approximately 600°F (316°C).

General Properties

Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).

Applications & Standards

Applications	Standards
Offshore (foils, helicopter deck platforms, etc.) Food industry Pulp and paper industry Aerospace (turbine blades, etc.) Mechanical components Nuclear waste casks	ASTM A693 grade 630 (AMS 5604B) UNS S17400 EURONORM 1.4542 X5CrNiCuNb 16-4 AFNOR Z5 CNU 17-4PH DIN 1.4542

Chemical Composition

Element	Content (%)
C	max 0.07
Mn	max 1
Si	max 1
P	max 0.04
S	max 0.030
Cr	15 - 17.5
Ni	3 - 5
Cu	3 - 5
Nb+Ta	0.15 - 0.45

Mechanical Properties

Condition	Tensile Strength (MPa)	Yield Strength 0.2% Proof (MPa)	Elongation (% in 50mm)	Hardness Rockwell C (HR C)
Solution Treated	1105 typ	1000 typ	15 typ	38 max
Condition 900	1310 min	1170 min	10 min	40 min
Condition 1150	930 min	724 min	16 min	28 min

Physical Properties

Property	Value
Density (kg/m³)	7750
Thermal Conductivity at 100°C (W/m.K)	18.4
Thermal Conductivity at 500°C (W/m.K)	22.7
Specific Heat 0-100°C (J/kg.K)	460
Electrical Resistivity (nΩ.m)	800