ASTM A276 Standard 17-4PH Stainless Steel Bright Bar Hot Rolled with OD 3-300mm

証明	ISO, AISI, ASTM, EN, DIN, JIS
最小注文数量	50 kg
価格	US $3.13-3.61 / kg

商品の詳細

形	ラウンド	技術	熱間圧延
表面処理	明るい	直径	8～450mm
長さ	6メートル/個	メイングレード	201 301 303Cu 304 304L 309S 310S 316L 316Ti 317L 318 321 347 410 420 430 431 440a/b/c 904L 2205 2507
抗張力	1105～1310MPa	降伏強さ	724～1300MPa
伸長	10-16%	硬度	28-44HRC
密度	7750kg/m3	熱伝導率	18.4-22.7W/mK
比熱	460 J/kg.K	電気抵抗率	800nΩ・m
最高温度	572°F（300°C）
ハイライト	ASTM A276 Standard Stainless Steel Bright Bar , OD 3-300mm 17-4PH Stainless Steel Bar , Hot Rolled Polished Stainless Steel Bar

メッセージ

製品の説明

ASTM A276 Standard 17-4PH Stainless Steel Bright Bar

High-quality polished stainless steel bars manufactured to ASTM standards, available in various diameters and finishes.

Product Specifications

Products	17-4PH Stainless Steel Round Bar
Standard	ASTM GB DIN EN
Diameter	8 - 450mm
Length	6m /pcs or cutting as request
Finishing	Black Bar / Bright Bar
Main Grades	201, 301, 303Cu, 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 318, 321, 347, 410, 420, 430, 431, 440a/b/c, 904L, 2205, 2507, Hastelloy C276, C4, C22, Inconel 600, 625, Incoloy 800, 825, 825H, etc.
Service	Cutting, surface polishing, heat treatment
Brand	Walsin, BAOSTEEL, TISCO, QINGSHAN

Material Description

17-4PH Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel designed for applications requiring high strength and moderate corrosion resistance. This alloy maintains high strength up to approximately 600°F (316°C).

General Properties

Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with copper and niobium additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).

Applications & Standards

Applications	Standards
Offshore (foils, helicopter deck platforms) Food industry Pulp and paper industry Aerospace (turbine blades) Mechanical components Nuclear waste casks	ASTM A693 grade 630 (AMS 5604B) UNS S17400 EURONORM 1.4542 X5CrNiCuNb 16-4 AFNOR Z5 CNU 17-4PH DIN 1.4542

Chemical Composition

Composition of 17-4PH Stainless Steel

Grade	C	Mn	Si	P	S	Cr	Ni	Cu	Nb+Ta
630	min. max: - 0.07	- 1	- 1	- 0.04	- 0.030	15 17.5	3 5	3 5	0.15 0.45

Mechanical Properties

Condition	Tensile Strength (MPa)	Yield Strength 0.2% Proof (MPa)	Elongation (% in 50mm)	Hardness Rockwell C (HR C)	Hardness Brinell (HB)
Solution Treated	1105 typ	1000 typ	15 typ	38 max	363 max
Condition 900	1310 min	1170 min	10 min	40 min	388 min
Condition 1150	930 min	724 min	16 min	28 min	277 min

Physical Properties

Mean Co-eff of Thermal Expansion (µm/m/°C)	Thermal Conductivity (W/m.K)	Specific Heat 0-100°C (J/kg.K)	Electrical Resistivity (nΩ.m)
0-100°C: 10.8 0-315°C: 11.6 0-538°C: -	At 100°C: 18.4 At 500°C: 22.7	460	800

Product Images

Applications

Engine components
High strength and boat propeller shafts
Plastic moulding dies
Valves and gears

Contact Information

札:

ASTM A276 Standard 17-4PH Stainless Steel Bright Bar Hot Rolled with OD 3-300mm

ASTM A276 Standard Stainless Steel Bright Bar

OD 3-300mm 17-4PH Stainless Steel Bar

Hot Rolled Polished Stainless Steel Bar