Hot Rolled 17-4PH Stainless Steel Round Bar with Bright Surface and OD 6-300mm

Certification	ISO, AISI, ASTM, EN, DIN, JIS
Minimum Order Quantity	50 kg
Price	US $3.48-3.97 / kg

Product Details

Model NO.	17-4PH/630	Shape	Round
Technique	Hot Rolled	Surface Treatment	Bright
Specification	OD 6-300mm	Diameter	8 - 450mm
Length	6m /pcs Or Cutting As Request	Tensile Strength	1105-1310 MPa
Yield Strength	1000-1170 MPa	Elongation	10-16%
Hardness	28-44 HRC	Density	7750 Kg/m³
Thermal Conductivity	18.4-22.7 W/m.K	Specific Heat	460 J/kg.K
Electrical Resistivity	800 NΩ.m
Highlight	Hot Rolled 17-4PH Stainless Steel Round Bar , Bright Surface 17-4PH Stainless Steel Rod , OD 6-300mm 17-4PH Stainless Steel Shaft

Leave a Message

Product Description

Grade 17-4PH Stainless Steel Round Bar / Rod / Shaft

High-strength precipitation hardening stainless steel offering excellent mechanical properties and moderate corrosion resistance for demanding industrial applications.

Product Specifications

Product	17-4PH Stainless Steel Round Bar
Standard	ASTM GB DIN EN
Diameter	8 - 450mm
Length	6m /pcs or cutting as requested
Finishing	Black Bar / Bright Bar
Main Grades	201, 301, 303Cu, 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 318, 321, 347, 410, 420, 430, 431, 440a/b/c, 904L, 2205, 2507, Hastelloy C276, C4, C22, Inconel 600, 625, Incoloy 800, 825, 825H, etc.
Service	Cutting, surface polishing, heat treatment
Brand	Walsin, BAOSTEEL, TISCO, QINGSHAN

Material Description

17-4PH (Type 630) is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and moderate corrosion resistance. High strength is maintained to approximately 600°F (316°C).

General Properties

Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).

Applications & Standards

Applications	Standards
Offshore (foils, helicopter deck platforms) Food industry Pulp and paper industry Aerospace (turbine blades) Mechanical components Nuclear waste casks	ASTM A693 grade 630 (AMS 5604B) UNS S17400 EURONORM 1.4542 X5CrNiCuNb 16-4 AFNOR Z5 CNU 17-4PH DIN 1.4542

Chemical Composition

Grade	C	Mn	Si	P	S	Cr	Ni	Cu	Nb+Ta
630	0.07 max	1.0 max	1.0 max	0.04 max	0.030 max	15-17.5	3-5	3-5	0.15-0.45

Mechanical Properties

Condition	Tensile Strength (MPa)	Yield Strength 0.2% Proof (MPa)	Elongation (% in 50mm)	Hardness Rockwell C (HR C)	Hardness Brinell (HB)
Solution Treated	1105 typ	1000 typ	15 typ	38 max	363 max
Condition 900	1310 min	1170 min	10 min	40 min	388 min
Condition 1150	930 min	724 min	16 min	28 min	277 min

Physical Properties

Property	Value
Density	7750 kg/m³
Thermal Conductivity at 100°C	18.4 W/m·K
Thermal Conductivity at 500°C	22.7 W/m·K
Specific Heat 0-100°C	460 J/kg·K
Electrical Resistivity	800 nΩ·m
Mean Coefficient of Thermal Expansion 0-100°C	10.8 µm/m·°C
Mean Coefficient of Thermal Expansion 0-315°C	11.6 µm/m·°C

Grade Specifications

Grade	UNS No	Euronorm	Japanese JIS
630	S17400	1.4542 X5CrNiCuNb16-4	SUS 630

Alternative Grade Comparison

Alternative Grade	Reasons for Choosing 17-4PH (630)
431	431 has higher toughness than 17-4PH. Better availability in some sizes.
416	Free-machining martensitic stainless steel - better for repetition machining. Lower cost.
316	Higher corrosion resistance to resist more severe environments, but with much lower strength than 17-4PH.
2205	Much better corrosion resistance than 17-4PH, with lower strength (but not as low as 316).

Heat Treatment

Solution treatment (Condition A): Grade 630 stainless steels are heated at 1040°C for 0.5 h, then air-cooled to 30°C. Small sections can be oil quenched.

Hardening: Grade 630 stainless steels are age-hardened at low temperatures to achieve required mechanical properties.

Condition	Hardening Temp (°C)	Time (h)	Typical Hardness Rockwell C	Tensile Strength (MPa)
A	Ann	-	36	1100
H900	482	1	44	-
H925	496	4	42	1170-1320
H1025	552	4	38	1070-1220
H1075	580	4	36	1000-1150
H1100	593	4	35	970-1120
H1150	621	4	33	930-1080

Fabrication

Welding

Grade 630 stainless steels can be welded using all conventional methods and do not require pre-heating. Care should be taken in designing and welding high strength steels to prevent weldment stresses.

Machining

Grade 630 stainless steels can be machined in their solution-treated condition. They have machining rates similar to grade 304 steels.