Bright Polished 17-4PH Stainless Steel Bar with Solid Solution Finishing Diameter 10-50mm in Stock
Product Details
| Shape | Round | Technique | Hot Rolled |
|---|---|---|---|
| Surface Treatment | Bright | Diameter Range | 8 - 450mm |
| Length | 6m /pcs | Main Grades | 201 301 303Cu 304 304L 309S 310S 316L 316Ti 317L 318 321 347 410 420 430 431 440a/b/c 904L 2205 2507 |
| Tensile Strength | 1105 - 1310 MPa | Yield Strength | 1000 - 1170 MPa |
| Elongation | 10 - 16% | Hardness | 28 - 44 HRC |
| Density | 7750 Kg/m³ | Thermal Conductivity | 18.4 - 22.7 W/m.K |
| Specific Heat | 460 J/kg.K | Electrical Resistivity | 800 NΩ.m |
| Coeff Thermal Expansion | 10.8 - 11.6 µm/m/°C | ||
| Highlight | Bright Polished 17-4PH Stainless Steel Bar,Diameter 10-50mm 630 Stainless Steel Bar,Solid Solution Finishing Precipitation Hardening Stainless Steel Bar |
||
Product Description
Bright Polished 17-4PH Stainless Steel Bar
Diameter 10-50mm in stock with solid solution finishing
Product Specifications
| Product | 17-4PH Stainless Steel Round Bar |
|---|---|
| Standard | ASTM GB DIN EN |
| Diameter | 8 - 450mm |
| Length | 6m /pcs or cutting as requested |
| Finishing | Black Bar / Bright Bar |
| Main Grades | 201, 301, 303Cu, 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 318, 321, 347, 410, 420, 430, 431, 440a/b/c, 904L, 2205, 2507, Hastelloy C276, C4, C22, Inconel 600, 625, Incoloy 800, 825, 825H, etc. |
| Service | Cutting, surface polishing, heat treatment |
| Brand | Walsin, BAOSTEEL, TISCO, QINGSHAN |
Material Description
17-4 Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and moderate corrosion resistance. High strength is maintained to approximately 600°F (316°C).
General Properties
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
Applications & Standards
| Applications | Standards |
|---|---|
|
|
Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Ni | Cu | Nb+Ta |
|---|---|---|---|---|---|---|---|---|---|
| 630 | 0.07 max | 1.0 max | 1.0 max | 0.04 max | 0.030 max | 15-17.5 | 3-5 | 3-5 | 0.15-0.45 |
Mechanical Properties
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C (HRC) | Hardness Brinell (HB) |
|---|---|---|---|---|---|
| Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max | 363 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min | 388 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min | 277 min |
Physical Properties
| Property | Value |
|---|---|
| Density | 7750 kg/m³ |
| Mean Coefficient of Thermal Expansion (0-100°C) | 10.8 µm/m/°C |
| Mean Coefficient of Thermal Expansion (0-315°C) | 11.6 µm/m/°C |
| Thermal Conductivity at 100°C | 18.4 W/m·K |
| Thermal Conductivity at 500°C | 22.7 W/m·K |
| Specific Heat (0-100°C) | 460 J/kg·K |
| Electrical Resistivity | 800 nΩ·m |
Product Images
Applications
- Engine components
- High strength boat propeller shafts
- Plastic moulding dies
- Valves and gears