Bright Annealing 17-4PH Stainless Steel Round Bar Hot Rolled with Diameter 10-300mm

Certification	ISO, AISI, ASTM, EN, DIN, JIS
Minimum Order Quantity	50 kg
Price	US $3.33-3.79 / kg

Product Details

Shape	Round	Technique	Hot Rolled
Surface Treatment	Bright	Diameter Range	8 - 450mm
Length	6m /pcs	Main Grades	201, 301, 303Cu, 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 318, 321, 347, 410, 420, 430, 431, 440a/b/c, 904L, 2205, 2507
Tensile Strength	1105-1310 MPa	Yield Strength	1000-1170 MPa
Elongation	10-16%	Hardness	28-44 HRC
Density	7750 Kg/m³	Thermal Conductivity	18.4-22.7 W/m.K
Specific Heat	460 J/kg.K	Electrical Resistivity	800 NΩ.m
Max Temperature	572°F (300°C)
Highlight	Bright Annealing Stainless Steel Round Bar , Hot Rolled 17-4PH Stainless Steel Bar , Diameter 10-300mm 630 Stainless Steel Bar

Leave a Message

Product Description

Bright Annealing 17-4PH Stainless Steel Shaft

Diameter range: 10 - 300mm SS Bar

Product Specifications

Products	17-4PH Stainless Steel Round Bar
Standard	ASTM GB DIN EN
Diameter	8 - 450mm
Length	6m /pcs or cutting as request
Finishing	black bar / Bright Bar
Main Grade	201 301 303Cu 304 304L 309S 310S 316L 316Ti 317L 318 321 347 410 420 430 431 440a/b/c 904L 2205 2507 Hastelloy C276 C4 C22 Inconel 600 625 Incoloy 800 825 825H etc.
Service	Cutting, surface polishing, heat treatment
Brand	Walsin BAOSTEEL TISCO QINGSHAN

Material Description

17-4 Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and moderate corrosion resistance. High strength is maintained to approximately 600°F (316°C).

General Properties

Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).

Applications & Standards

Applications	Standards
Offshore (foils, helicopter deck platforms) Food industry Pulp and paper industry Aerospace (turbine blades) Mechanical components Nuclear waste casks	ASTM A693 grade 630 (AMS 5604B) UNS S17400 EURONORM 1.4542 X5CrNiCuNb 16-4 AFNOR Z5 CNU 17-4PH DIN 1.4542

Chemical Composition

Grade	C	Mn	Si	P	S	Cr	Ni	Cu	Nb+Ta
630	0.07 max	1.0 max	1.0 max	0.04 max	0.030 max	15-17.5	3-5	3-5	0.15-0.45

Mechanical Properties

Condition	Tensile Strength (MPa)	Yield Strength 0.2% Proof (MPa)	Elongation (% in 50mm)	Hardness Rockwell C (HR C)	Hardness Brinell (HB)
Solution Treated	1105 typ	1000 typ	15 typ	38 max	363 max
Condition 900	1310 min	1170 min	10 min	40 min	388 min
Condition 1150	930 min	724 min	16 min	28 min	277 min

Physical Properties

Mean Co-eff of Thermal Expansion (µm/m/°C)	Thermal Conductivity (W/m.K)	Specific Heat 0-100°C (J/kg.K)	Electrical Resistivity (nΩ.m)
10.8 (0-100°C) 11.6 (0-315°C)	18.4 (At 100°C) 22.7 (At 500°C)	460	800

Alternative Grades

Grade	Reasons for choosing 17/4PH (630)
431	431 Has higher toughness than 17/4PH. Better availability in some sizes.
416	Free-machining martensitic stainless steel - better for repetition machining. Lower cost.
316	Higher corrosion resistance of 316 to resist more severe environments, but with much lower strength than 17/4PH.
2205	Much better corrosion resistance than 17/4PH, with a lower strength (but not as low as 316).