Bright Polished 17-4PH Stainless Steel Shaft with OD 3-300mm and Precipitation Hardening
Product Details
| Shape | Round | Technique | Hot Rolled |
|---|---|---|---|
| Surface Treatment | Bright | Diameter Range | 8 - 450mm |
| Length | 6m /pcs | Main Grades | 201 301 303Cu 304 304L 309S 310S 316L 316Ti 317L 318 321 347 410 420 430 431 440a/b/c 904L 2205 2507 |
| Tensile Strength | 1105-1310 MPa | Yield Strength | 1000-1170 MPa |
| Elongation | 10-16% | Hardness | 28-44 HRC |
| Density | 7750 Kg/m³ | Thermal Conductivity | 18.4-22.7 W/m.K |
| Specific Heat | 460 J/kg.K | Electrical Resistivity | 800 NΩ.m |
| Coefficient Of Thermal Expansion | 10.8-11.6 µm/m/°C | ||
| Highlight | Bright Polished Stainless Steel Shaft,OD 3-300mm 17-4PH Stainless Steel Round Bar,Precipitation Hardening 630 Stainless Steel Bar |
||
Product Description
Bright Polished Stainless Steel Shaft Grade 630 / 17-4PH / 1.4542
High-strength precipitation hardening stainless steel shaft with excellent corrosion resistance and mechanical properties.
Product Specifications
| Products | 17-4PH Stainless Steel Round Bar |
|---|---|
| Standard | ASTM GB DIN EN |
| Diameter | 8 - 450mm |
| Length | 6m /pcs or cutting as request |
| Finishing | black bar / Bright Bar |
| Main Grades | 201 301 303Cu 304 304L 309S 310S 316L 316Ti 317L 318 321 347 410 420 430 431 440a/b/c 904L 2205 2507 Hastelloy C276 C4 C22 Inconel 600 625 Incoloy 800 825 825H etc. |
| Service | Cutting, surface polishing, heat treatment |
| Brand | Walsin BAOSTEEL TISCO QINGSHAN |
Material Description
17-4PH Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and moderate corrosion resistance. High strength is maintained to approximately 600°F (316°C).
General Properties
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
Applications & Standards
| Applications | Standards |
|---|---|
|
|
Chemical Composition
| Element | Content (%) |
|---|---|
| C | ≤ 0.07 |
| Mn | ≤ 1.00 |
| Si | ≤ 1.00 |
| P | ≤ 0.04 |
| S | ≤ 0.030 |
| Cr | 15.0 - 17.5 |
| Ni | 3.0 - 5.0 |
| Cu | 3.0 - 5.0 |
| Nb+Ta | 0.15 - 0.45 |
Mechanical Properties
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C (HR C) |
|---|---|---|---|---|
| Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min |
Physical Properties
| Property | Value |
|---|---|
| Density | 7750 kg/m³ |
| Thermal Conductivity at 100°C | 18.4 W/m·K |
| Thermal Conductivity at 500°C | 22.7 W/m·K |
| Specific Heat 0-100°C | 460 J/kg·K |
| Electrical Resistivity | 800 nΩ·m |
| Mean Coefficient of Thermal Expansion (0-100°C) | 10.8 µm/m·°C |
Product Images
Applications
- Engine components
- High strength and boat propeller shafts
- Plastic moulding dies
- Valves and gears