Hot Rolled UNS S17400 17-4PH Stainless Steel Bar with Bright Surface and OD 6-300mm

Certification	ISO, AISI, ASTM, EN, DIN, JIS
Minimum Order Quantity	50 kg
Price	US $3.31-3.8 / kg

Product Details

Model NO.	17-4PH/630	Shape	Round
Technique	Hot Rolled	Surface Treatment	Bright
Specification	OD 6-300mm	Diameter	8 - 450mm
Length	6m /pcs	Tensile Strength	1105-1310 MPa
Yield Strength	1000-1170 MPa	Elongation	10-16%
Hardness	28-44 HRC	Density	7750 Kg/m³
Thermal Conductivity	18.4-22.7 W/m.K	Electrical Resistivity	800 NΩ.m
Max Temperature	572°F (300°C)
Highlight	Hot Rolled Stainless Steel Bar , Bright Surface 17-4PH Stainless Steel Rod , OD 6-300mm UNS S17400 Round Bar

Leave a Message

Product Description

UNS S17400 Alloy 17-4PH Stainless Steel Bar / Black Stainless Steel Rod

Product Specifications

Products	17-4PH Stainless Steel Round Bar
Standard	ASTM GB DIN EN
Diameter	8 - 450mm
Length	6m /pcs or cutting as request
Finishing	black bar / Bright Bar
Main Grades	201 301 303Cu 304 304L 309S 310S 316L 316Ti 317L 318 321 347 410 420 430 431 440a/b/c 904L 2205 2507 Hastelloy C276 C4 C22 Inconel 600 625 Incoloy 800 825 825H
Service	Cutting, surface polishing, heat treatment
Brand	Walsin BAOSTEEL TISCO QINGSHAN

Material Description

17-4 Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and moderate corrosion resistance. High strength is maintained to approximately 600°F (316°C).

General Properties

Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).

Applications & Standards

Applications	Standards
Offshore (foils, helicopter deck platforms) Food industry Pulp and paper industry Aerospace (turbine blades) Mechanical components Nuclear waste casks	ASTM A693 grade 630 (AMS 5604B) UNS S17400 EURONORM 1.4542 X5CrNiCuNb 16-4 AFNOR Z5 CNU 17-4PH DIN 1.4542

Chemical Composition

Element	Content (%)
C	0.07 max
Mn	1.0 max
Si	1.0 max
P	0.04 max
S	0.030 max
Cr	15.0 - 17.5
Ni	3.0 - 5.0
Cu	3.0 - 5.0
Nb+Ta	0.15 - 0.45

Mechanical Properties

Condition	Tensile Strength (MPa)	Yield Strength 0.2% Proof (MPa)	Elongation (% in 50mm)	Hardness Rockwell C (HRC)
Solution Treated	1105 typ	1000 typ	15 typ	38 max
Condition 900	1310 min	1170 min	10 min	40 min
Condition 1150	930 min	724 min	16 min	28 min

Physical Properties

Property	Value
Density	7750 kg/m³
Thermal Conductivity at 100°C	18.4 W/m·K
Thermal Conductivity at 500°C	22.7 W/m·K
Specific Heat 0-100°C	460 J/kg·K
Electrical Resistivity	800 nΩ·m

Alternative Grade Comparison

Alternative Grade	Reason for Choosing 17-4PH
431	431 has higher toughness than 17-4PH
416	Free-machining martensitic stainless steel - better for repetition machining
316	Higher corrosion resistance but with much lower strength
2205	Much better corrosion resistance with lower strength