Hot Rolled Bright Surface 17-4PH Stainless Steel Rod and Bar with OD 6-300mm

Certification	ISO, AISI, ASTM, EN, DIN, JIS
Minimum Order Quantity	50 kg
Price	US $3.37-3.86 / kg

Product Details

Model NO.	17-4PH/630	Shape	Round
Technique	Hot Rolled	Surface Treatment	Bright
Specification	OD 6-300mm	Diameter	8 - 450mm
Length	6m /pcs Or Cutting As Request	Tensile Strength	1105-1310 MPa
Yield Strength	724-1170 MPa	Elongation	10-16%
Hardness	28-44 HRC	Thermal Conductivity	18.4-22.7 W/m.K
Specific Heat	460 J/kg.K	Elec Resistivity	800 NΩ.m
Density	7750 Kg/m³
Highlight	Hot Rolled Stainless Steel Rod , Bright Surface Stainless Steel Bar , OD 6-300mm 17-4PH Stainless Steel

Leave a Message

Product Description

ASTM A276 17-4PH / 1.4542 / S17400 Stainless Steel Rod / Bar

Product Specification

Products	17-4PH Stainless Steel Round Bar
Standard	ASTM GB DIN EN
Diameter	8 - 450mm
Length	6m /pcs or cutting as request
Finishing	black bar / Bright Bar
Main Grade	201 301 303Cu 304 304L 309S 310S 316L 316Ti 317L 318 321 347 410 420 430 431 440a/b/c 904L 2205 2507 Hastelloy C276 C4 C22 Inconel 600 625 Incoloy 800 825 825H.etc
Service	Cutting, surface polishing, heat treatment
Brand	Walsin BAOSTEEL TISCO QINGSHAN

Material Description

17-4PH Stainless Steel (also known as Type 630) is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and moderate corrosion resistance. High strength is maintained to approximately 600°F (316°C).

General Properties

Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).

Applications & Standards

Applications	Standards
Offshore (foils, helicopter deck platforms) Food industry Pulp and paper industry Aerospace (turbine blades) Mechanical components Nuclear waste casks	ASTM A693 grade 630 (AMS 5604B) UNS S17400 EURONORM 1.4542 X5CrNiCuNb 16-4 AFNOR Z5 CNU 17-4PH DIN 1.4542

Chemical Composition

Grade	C	Mn	Si	P	S	Cr	Ni	Cu	Nb+Ta
630	min. max - 0.07	- 1	- 1	- 0.04	- 0.030	15 17.5	3 5	3 5	0.15 0.45

Mechanical Properties

Condition	Tensile Strength (MPa)	Yield Strength 0.2% Proof (MPa)	Elongation (% in 50mm)	Hardness Rockwell C (HR C)	Hardness Brinell (HB)
Solution Treated	1105 typ	1000 typ	15 typ	38 max	363 max
Condition 900	1310 min	1170 min	10 min	40 min	388 min
Condition 1150	930 min	724 min	16 min	28 min	277 min

Physical Properties

Mean Co-eff of Thermal Expansion (µm/m/°C)	Thermal Conductivity (W/m.K)	Specific Heat 0-100°C (J/kg.K)	Elec Resistivity (nΩ.m)
0-100°C: 10.8 0-315°C: 11.6 0-538°C: -	At 100°C: 18.4 At 500°C: 22.7	460	800

Grade Specification Comparison

Grade	UNS No	Euronorm	Japanese JIS
630	S17400	1.4542 X5CrNiCuNb16-4	SUS 630

Alternative Grades Comparison

Grade	Reasons for choosing 17/4PH (630)
431	431 Has higher toughness than 17/4PH. Better availability in some sizes.
416	Free-machining martensitic stainless steel - better for repetition machining. Lower cost.
316	Higher corrosion resistance of 316 to resist more severe environments, but with much lower strength than 17/4PH.
2205	Much better corrosion resistance than 17/4PH, with a lower strength (but not as low as 316).

Corrosion Resistance

Grade 630 stainless steels have good corrosion resistance in many environments. They exhibit improved resistance against stress corrosion cracking when aged at 550°C or more. However, grade 630 steels are less resistant in solution treated Condition A and should not be used in this condition despite considerable hardness.

Heat Resistance

Grade 630 stainless steels have good resistance to oxidation. However, long-time exposure to temperatures of 370 to 480°C should be avoided to prevent loss of toughness at ambient temperature. These grades should not be used above age-hardening temperature to avoid reduction of hardness and mechanical properties.

Heat Treatment

Solution treatment (Condition A) - Grade 630 stainless steels are heated at 1040°C for 0.5 h, then air-cooled to 30°C. Small sections can be oil quenched.

Hardening - Grade 630 stainless steels are age-hardened at low temperatures to achieve required mechanical properties. During the process, superficial discoloration occurs followed by shrinkage.

Condition	Hardening Temp (°C)	Time (h)	Typical Hardness Rockwell C	Tensile Strength (MPa)
A	Ann	-	36	1100
H900	482	1	44	-
H925	496	4	42	1170-1320
H1025	552	4	38	1070-1220
H1075	580	4	36	1000-1150
H1100	593	4	35	970-1120
H1150	621	4	33	930-1080

Welding & Machining

Welding: Grade 630 stainless steels can be welded using all conventional methods without pre-heating. Care should be taken in designing and welding of high strength steels to prevent weldment stresses.

Machining: Grade 630 stainless steels can be machined in their solution-treated condition. They have machining rates similar to grade 304 steels.

Product Applications