Grade AISI1020 ASTM A519 Carbon Steel Pipe for Structure Heavy Wall Seamless Steel Tube

Machinability

AISI SAE 1020 carbon steel machinability rating is 65 based on a machinability rating of 100% for 1212 steel.

SAE AISI 1020 Steel Heat Treatment

The heat treatment of SAE AISI 1020 mild steel including normalizing, annealing, austenitizing, etc.

Normalizing of AISI 1020

The typical normalizing temperature for SAE AISI 1020 mild steel is 915 °C (1675 °F).

Annealing of AISI 1020

Recommended temperature and cooling cycle for full annealing of small carbon steel forgings (size ≤ 3 in.):

Annealing temperature is 855-900 °C (1575-1650 °F), cooling cycle is from 855 °C (1575 °F) to 700 °C (1290 °F), furnace cooling speed at 28 °C/h (50 °F/h), Brinell hardness is 111-149 HB.

Reheating (Austenitizing)

Reheating (austenitizing) temperatures for hardening of SAE 1020 steel is 760-790 °C (1400-1450 °F). Carburizing is commonly carried out at 900 to 925 °C (1650 to 1700 °F).

Case Hardening

The surface hardening carburization temperature of 1020 carbon steel is 970-955 °C, and most of them are carried out in a mixed gas of methane and carrier gas. Hardening after carburizing is usually achieved by direct quenching from the carburizing temperature into water or brine.

Typical heat treatment for SAE 1020 case hardening

• Carbon temperature: 900-925 °C (1650-1700 °F), cooling method: water or caustic;
• Reheat temperature: 790 °C (1450 °F), cooling method: water or 3% sodium hydroxide;
• Carbonitriding temperature: 790-900 °C (1450-1650 °F), cooling method: oil;
• Temper temperature: 120-205 °C (250-400 °F), for stress relief and improving resistance to cracking (not mandatory).

Typical Forging Temperature

Typical forging temperature for AISI 1020 mild steel is 1290 °C (2350 °F).

AISI 1020 Carbon Steel Welding

The recommended preheat and interpass temperatures for AISI SAE C1020 steel:

For thickness ≤50mm (2 in.), the recommended preheat and interpass temperature is above -12 °C (for low hydrogen); and 38 °C for other than low hydrogen.

For thickness (t) 50< t ≤100, the recommended preheat and interpass temperature is 93 °C (for low hydrogen); and 150 °C (for other than low hydrogen).

Postweld heat treatment is optional, temperature is 590-675 °C (1100-1250 °F).

Application

ASTM AISI SAE 1020 steel has many semi-finished products, such as square steel bars, flat steel bars, round steel bars, steel plates, which can be used to make truck, automotive and agricultural equipment parts such as axles, mechanical parts, cold head bolts, motor shafts, pump shafts, ratchet, light gear, gear drives, worm gear, spindle, seat bracket, crane-cable drum, motor-brake wheel, etc. And usually also made into steel channels, steel angles, I-beams and H-beams.

AISI SAE ASTM 1020 Steel Equivalent Material

SAE ASTM AISI 1020 carbon steel equivalent to European EN (Germany DIN EN, British BSI, French NF…), Japanese JISand Chinese GB standard.