All Products
-
Raian IonescuMaterial quality very good. we have cooperate more than 10 Years. They trade lots kinds of steel material. All material quality good. They duty for all material quality. We are planing continue cooperate with them in the future
Alloy 630 Stainless Steel Round Bar Diameter 4-800mm with Precipitation Hardening and Bright Surface
Product Details
| Model NO. | 17-4PH/630 | Shape | Round |
|---|---|---|---|
| Technique | Hot Rolled | Surface Treatment | Bright |
| Specification | OD 6-300mm | Diameter | 8 - 450mm |
| Length | 6m /pcs | Main Grade | 201 301 303Cu 304 304L 309S 310S 316L 316Ti 317L 318 321 347 410 420 430 431 440a/b/c 904L 2205 2507 |
| Tensile Strength | 1105-1310 MPa | Yield Strength | 1000-1170 MPa |
| Elongation | 10-16% | Hardness | 28-44 HRC |
| Density | 7750 Kg/m³ | Thermal Conductivity | 18.4-22.7 W/m.K |
| Electrical Resistivity | 800 NΩ.m | ||
| Highlight | Diameter 4-800mm Stainless Steel Round Bar,Precipitation Hardening 17-4PH Stainless Steel Bar,Bright Surface 630 Stainless Steel Bar |
||
Product Description
Alloy 630 Stainless Steel Solid Bar
Diameter 4-800mm | PH Grades 17-4PH
Product Specifications
| Products | 17-4PH Stainless Steel Round Bar |
|---|---|
| Standard | ASTM GB DIN EN |
| Diameter | 8 - 450mm |
| Length | 6m /pcs or cutting as request |
| Finishing | black bar / Bright Bar |
| Main Grades | 201 301 303Cu 304 304L 309S 310S 316L 316Ti 317L 318 321 347 410 420 430 431 440a/b/c 904L 2205 2507 Hastelloy C276 C4 C22 Inconel 600 625 Incoloy 800 825 825H etc |
| Service | Cutting, surface polishing, heat treatment |
| Brand | Walsin BAOSTEEL TISCO QINGSHAN |
Material Description
17-4 Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and moderate corrosion resistance. High strength is maintained to approximately 600°F (316°C).
General Properties
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
Applications & Standards
| Applications | Standards |
|---|---|
|
|
Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Ni | Cu | Nb+Ta |
|---|---|---|---|---|---|---|---|---|---|
| 630 | 0.07 max | 1.0 max | 1.0 max | 0.04 max | 0.030 max | 15-17.5 | 3-5 | 3-5 | 0.15-0.45 |
Mechanical Properties
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C (HR C) | Hardness Brinell (HB) |
|---|---|---|---|---|---|
| Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max | 363 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min | 388 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min | 277 min |
Physical Properties
| Property | Value |
|---|---|
| Density (kg/m³) | 7750 |
| Thermal Expansion 0-100°C (µm/m/°C) | 10.8 |
| Thermal Expansion 0-315°C (µm/m/°C) | 11.6 |
| Thermal Conductivity at 100°C (W/m.K) | 18.4 |
| Thermal Conductivity at 500°C (W/m.K) | 22.7 |
| Specific Heat 0-100°C (J/kg.K) | 460 |
| Electrical Resistivity (nΩ.m) | 800 |
Alternative Grade Comparisons
| Alternative Grade | Reasons for Choosing 17-4PH (630) |
|---|---|
| 431 | 431 has higher toughness than 17-4PH. Better availability in some sizes. |
| 416 | Free-machining martensitic stainless steel - better for repetition machining. Lower cost. |
| 316 | Higher corrosion resistance of 316 to resist more severe environments, but with much lower strength than 17-4PH. |
| 2205 | Much better corrosion resistance than 17-4PH, with a lower strength (but not as low as 316). |
Product Images
Applications
- Engine components
- High strength and boat propeller shafts
- Plastic moulding dies
- Valves and gears
Recommended Products