Hot Rolled 17-4PH Stainless Steel Round Bar with Bright Surface and OD 6-300mm

Certification	ISO, AISI, ASTM, EN, DIN, JIS
Minimum Order Quantity	50 kg
Price	US $3.18-3.67 / kg

Product Details

Model NO.	17-4PH/630	Shape	Round
Technique	Hot Rolled	Surface Treatment	Bright
Specification	OD 6-300mm	Diameter	8 - 450mm
Length	6m /pcs	Main Grade	201 301 303Cu 304 304L 309S 310S 316L 316Ti 317L 318 321 347 410 420 430 431 440a/b/c 904L 2205 2507
Tensile Strength	1105-1310 MPa	Yield Strength	724-1300 MPa
Elongation	10-16%	Hardness	28-44 HRC
Thermal Conductivity	18.4-22.7 W/m.K	Specific Heat	460 J/kg.K
Elec Resistivity	800 NΩ.m
Highlight	Hot Rolled 17-4PH Stainless Steel Round Bar , Bright Surface 630 Stainless Steel Round Bar , OD 6-300mm Precipitation Hardening Stainless Steel Round Bar

Leave a Message

Product Description

17-4PH Stainless Steel Round Bar

17-4 Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and moderate corrosion resistance. High strength is maintained to approximately 600°F (316°C).

Product Specifications

Product	17-4PH Stainless Steel Round Bar
Standard	ASTM GB DIN EN
Diameter	8 - 450mm
Length	6m /pcs or cutting as requested
Finishing	Black Bar / Bright Bar
Main Grades	201, 301, 303Cu, 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 318, 321, 347, 410, 420, 430, 431, 440a/b/c, 904L, 2205, 2507, Hastelloy C276, C4, C22, Inconel 600, 625, Incoloy 800, 825, 825H, etc.
Service	Cutting, surface polishing, heat treatment
Brand	Walsin, BAOSTEEL, TISCO, QINGSHAN

Material Description

Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).

Applications & Standards

Applications	Standards
Offshore (foils, helicopter deck platforms) Food industry Pulp and paper industry Aerospace (turbine blades) Mechanical components Nuclear waste casks	ASTM A693 grade 630 (AMS 5604B) UNS S17400 EURONORM 1.4542 X5CrNiCuNb 16-4 AFNOR Z5 CNU 17-4PH DIN 1.4542

Chemical Composition

Grade	C	Mn	Si	P	S	Cr	Ni	Cu	Nb+Ta
630	0.07 max	1.0 max	1.0 max	0.04 max	0.030 max	15-17.5	3-5	3-5	0.15-0.45

Mechanical Properties

Condition	Tensile Strength (MPa)	Yield Strength 0.2% Proof (MPa)	Elongation (% in 50mm)	Hardness Rockwell C (HR C)	Hardness Brinell (HB)
Solution Treated	1105 typ	1000 typ	15 typ	38 max	363 max
Condition 900	1310 min	1170 min	10 min	40 min	388 min
Condition 1150	930 min	724 min	16 min	28 min	277 min

Physical Properties

Property	Value
Density	7750 kg/m³
Mean Co-eff of Thermal Expansion (0-100°C)	10.8 µm/m/°C
Mean Co-eff of Thermal Expansion (0-315°C)	11.6 µm/m/°C
Thermal Conductivity (at 100°C)	18.4 W/m·K
Thermal Conductivity (at 500°C)	22.7 W/m·K
Specific Heat (0-100°C)	460 J/kg·K
Electrical Resistivity	800 nΩ·m

Alternative Grades Comparison

Alternative Grade	Reasons for Choosing 17-4PH (630)
431	431 has higher toughness than 17-4PH. Better availability in some sizes.
416	Free-machining martensitic stainless steel - better for repetition machining. Lower cost.
316	Higher corrosion resistance to resist more severe environments, but with much lower strength than 17-4PH.
2205	Much better corrosion resistance than 17-4PH, with lower strength (but not as low as 316).