Cold Rolled Stainless Steel Bright Bar with Bright Surface and OD 6-630mm SS 310 Round Bar
Product Details
| Model NO. | 310S 310 314 | Shape | Round |
|---|---|---|---|
| Technique | Cold Rolled | Surface Treatment | Bright |
| Specification | OD 6-630mm | Production Capacity | 50000kgs |
| Grade | 310S 314 310 | Diameter | 4.7 - 100mm |
| Length | 2000mm~6500mm | Tensile Strength | 540-740 MPa |
| Proof Strength | 250 MPa | Modulus Of Elasticity | 195 GPa |
| Elongation At Break | 40% | Hardness Brinell | 95 |
| Chemical Composition | Fe (Balance), Cr (24-26%), Ni (21-23%), Mo (2-2.50%), Mn (≤2%), N (0.10-0.16%), Si (≤0.70%), P (0.025%), C (≤0.020%), S (≤0.010%) | ||
| Highlight | Cold Rolled Stainless Steel Bright Bar,Bright Surface Stainless Steel Round Bar,OD 6-630mm SS 310 Round Bar |
||
Product Description
SS-310 310S 314 Stainless Steel Bright Bar
Product Specifications
| Product Name | Cold Drawn Stainless Steel Round Bar |
| Grade | 310S, 314, 310 |
| Standard | ASTM, JIS, DIN |
| Diameter | 4.7 - 100mm |
| Length | 2000mm - 6500mm or custom lengths available |
| Shape | Round Section |
| Surface | Cold Drawn |
| Place Of Origin | China (Mainland) |
Available Grades
201, 301, 303, 309S, 310S, 316L, 317L, 321, 410, 420, 440A/B/C, 2205, 2507, 904L, 17-4ph, 17-7ph, 15-5ph
Chemical Composition - Grade 310
| Element | Content (%) |
|---|---|
| Carbon (C) | ≤ 0.08 |
| Silicon (Si) | ≤ 1.0 |
| Manganese (Mn) | ≤ 2.0 |
| Chromium (Cr) | 24.0 - 26.0 |
| Nickel (Ni) | 19.0 - 21.0 |
| Phosphorus (P) | ≤ 0.045 |
| Sulfur (S) | 0.020 - 0.030 |
International Equivalents
DIN 1.4845, DIN X12CrNi25-21, DIN X8CrNi25-21, AFNOR Z12CN2520, BS 310S24, UNI X6CrNi2520, SS 2361, UNE F.331, SAE 310S, JIS SUH310, JIS SUS310S, JIS SUS310STP, JIS SUS310STPY, JIS SUS310STB, JIS SUS310SFB, EN X8CrNi25-21, EN 1.4845, UNS S31008
TP 310 / 310S Stainless Steel Technical Data
Chemical Composition - Grade 310 MoLN
| Element | Content (%) |
|---|---|
| Iron, Fe | Balance |
| Chromium, Cr | 24 - 26 |
| Nickel, Ni | 21 - 23 |
| Molybdenum, Mo | 2 - 2.50 |
| Manganese, Mn | ≤ 2 |
| Nitrogen, N | 0.10 - 0.16 |
| Silicon, Si | ≤ 0.70 |
| Phosphorous, P | 0.025 |
| Carbon, C | ≤ 0.020 |
| Sulfur, S | ≤ 0.010 |
Mechanical Properties - Grade 310 MoLN
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 540-740 MPa | 78,320-107,327 psi |
| Proof strength | 250 MPa | 36,259 psi |
| Modulus of elasticity (20°C) | 195 GPa | 28,282 ksi |
| Elongation at break | 40% | 40% |
| Hardness, Brinell | 95 | 95 |