Full Hard Cold Rolled 301 Stainless Steel Strip SS Coil Width 10-2000mm
Product Details
| Thickness | 0.1 - 3.0mm | Surface | 2B, Bright, Hairline |
|---|---|---|---|
| Width | 10 - 1219mm | Hardness | 1/4H, 1/2H, 3/4H, FH |
| Tensile Strength | 758 - 1276 MPa | Yield Strength | 276 - 965 MPa |
| Elongation | 9 - 60% | Density | 7880 Kg/m³ |
| Elastic Modulus | 193 GPa | Thermal Expansion | 16.9 μm/m/°C |
| Thermal Conductivity | 16.2 W/m.K | Specific Heat | 500 J/kg.K |
| Electrical Resistivity | 695 NΩ.m | Heat Resistance | Up To 900°C |
| Cold Working | 14MPa Per 1% Reduction | ||
| Highlight | Full Hard Stainless Steel Strip,Cold Rolled SS Coil,Width 10-2000mm 301 Stainless Steel Strip |
||
Product Description
301 Stainless Steel Strips - Full Hard & Spring Grade
High-strength 301 stainless steel strips available in various tempers including 1/4H, 1/2H, 3/4H, and Full Hard (FH). These spring-grade stainless steel strips offer exceptional strength and durability for demanding industrial applications.
Product Specifications
Material Grade: AISI 301 / 1.4319 / SUS301
Thickness Range: 0.1 - 3.0mm
Available Width: 10 - 1219mm
Surface Finish: 2B, Bright, Hairline
Hardness Options: 1/4H, 1/2H, 3/4H, FH or custom
Standards: ASTM A240 / JIS G4305 / EN 10088
Minimum Order: 300 Kgs
Material Overview
Grade 301 stainless steel is supplied as strips and wires with tensile strength up to 1800 MPa, available in tempers ranging from 1/16 Hard to Full Hard. This grade maintains sufficient ductility even in ½ hard conditions, making it ideal for aircraft components, rail car parts, and architectural structures. Higher tempers (¾ to full hard) provide excellent wear resistance and spring characteristics for simple form designs.
Grade Variants
301L: Low carbon version offering improved ductility (JIS G4305)
301LN: Higher nitrogen content with increased work hardening rate (EN10088-2 as 1.4318)
301LN: Higher nitrogen content with increased work hardening rate (EN10088-2 as 1.4318)
Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Ni | N |
|---|---|---|---|---|---|---|---|---|
| 301 ASTM A666 | ≤0.15 | ≤2.0 | ≤1.0 | ≤0.045 | ≤0.030 | 16.0-18.0 | 6.0-8.0 | ≤0.10 |
| 301L JIS G4305 | ≤0.03 | ≤2.0 | ≤1.0 | ≤0.045 | ≤0.030 | 16.0-18.0 | 6.0-8.0 | ≤0.20 |
| 1.4318/301LN EN 10088-2 | ≤0.03 | ≤2.0 | ≤1.0 | ≤0.045 | ≤0.015 | 16.5-18.5 | 6.0-8.0 | 0.10-0.20 |
Mechanical Properties
| Temper | Tensile Strength (MPa) min. | Yield Strength 0.2% Proof (MPa) min. | Elongation (% in 50mm) min. | Bend Angle (°) | Bend Factor |
|---|---|---|---|---|---|
| Annealed | 758 | 276 | 60 | - | - |
| 1/16 Hard | 620 | 310 | 40 | 180 | 1 |
| 1/8 Hard | 690 | 380 | 40 | 180 | 1 |
| 1/4 Hard | 862 | 514 | 25 | 90 | 2 |
| 1/2 Hard | 1034 | 758 | 18 | 90 | 2 |
| 3/4 Hard | 1205 | 930 | 12 | 90 | 3 |
| Full Hard | 1276 | 965 | 9 | 90 | 5 |
Physical Properties
| Property | Value |
|---|---|
| Density | 7880 kg/m³ |
| Elastic Modulus | 193 GPa |
| Thermal Expansion (0-100°C) | 16.9 μm/m/°C |
| Thermal Conductivity (100°C) | 16.2 W/m·K |
| Specific Heat | 500 J/kg·K |
| Electrical Resistivity | 695 nΩ·m |
Performance Characteristics
Corrosion Resistance
Similar corrosion resistance to 304 stainless steel, performing well in mildly corrosive environments at ambient temperatures.
Heat Resistance
Excellent oxidation resistance for intermittent service up to 840°C and continuous service up to 900°C.
Cold Working
High work hardening rate (approximately 14MPa increase per 1% reduction in area) enables achievement of high strength through cold rolling and forming operations. Non-magnetic when annealed, becomes magnetic when cold worked.
Welding
Suitable for all standard welding methods. Recommended filler metal: 308L. Annealing required after welding for maximum corrosion resistance (not necessary for 301L and 301LN variants).
Typical Applications
- Rail car structural components
- Air frame sections
- Highway trailer components
- Automotive wheel covers
- Wiper blade clips and holders
- Stove element clips
- Screen frames
- Toaster springs
- Curtain walls