Tutti i prodotti
  • JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
    Raian Ionescu
    Qualità materiale molto buona. abbiamo cooperare più di 10 anni. Vendono i generi dei lotti di materiale d'acciaio. Tutta la qualità materiale buona. Essi dovere per tutta la qualità materiale. Stiamo spianando per continuare a cooperare in futuro con loro
Persona di contatto : Gao
Numero di telefono : 18068357371
Whatsapp : +8618068357371

Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening

  • Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening
  • Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening
  • Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening
  • Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening
  • Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening
  • Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening
  • Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening
Certificazione ISO, AISI, ASTM, EN, DIN, JIS
Quantità di ordine minimo 50 kg
Prezzo US $3.3-3.82 / kg
Dettagli
Forma Girare Tecnica Laminato a caldo
Trattamento superficiale Luminoso Diametro 8-450 mm
Lunghezza 6 m/pz Grado principale 17-4ph
Resistenza alla trazione 1105 - 1310MPa Forza di snervamento 1000 - 1170MPa
Allungamento 10-16% Durezza 28 - 44 HRC
Densità 7750kg/m³ Conduttività termica 18,4 - 22,7 W/mK
Resistività elettrica 800 nΩ.m Coefficiente di espansione 10,8 - 11,6 µm/m/°C
Temperatura massima 572 ° F (300 ° C)
Evidenziare

Bright Polished Stainless Steel Round Bar

,

OD 3-300mm 17-4PH Stainless Steel Bar

,

Precipitation Hardening 630 Stainless Steel Bar
Lasciate un messaggio
Descrizione di prodotto
China Factory Direct Stainless Steel Bar - Grade 17-4PH / 630 / 1.4542
Precipitation hardening stainless steel bars with high strength and moderate corrosion resistance, maintained up to 600°F (316°C).
Product Specifications
Product17-4PH Stainless Steel Round Bar
StandardASTM GB DIN EN
Diameter8 - 450mm
Length6m /pcs or cutting as requested
FinishingBlack Bar / Bright Bar
Main Grades201, 301, 303Cu, 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 318, 321, 347, 410, 420, 430, 431, 440a/b/c, 904L, 2205, 2507, Hastelloy C276/C4/C22, Inconel 600/625, Incoloy 800/825/825H, etc.
ServiceCutting, surface polishing, heat treatment
BrandWalsin, BAOSTEEL, TISCO, QINGSHAN
Material Description
17-4PH (Type 630) is a chromium-copper precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. It combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance equivalent to Alloy 304 or 430 in most media.
Applications
  • Offshore (foils, helicopter deck platforms)
  • Food industry
  • Pulp and paper industry
  • Aerospace (turbine blades)
  • Mechanical components
  • Nuclear waste casks
Standards
  • ASTM A693 grade 630 (AMS 5604B) UNS S17400
  • EURONORM 1.4542 X5CrNiCuNb 16-4
  • AFNOR Z5 CNU 17-4PH
  • DIN 1.4542
Chemical Composition
ElementMinMax
C-0.07
Mn-1.00
Si-1.00
P-0.04
S-0.030
Cr15.0017.50
Ni3.005.00
Cu3.005.00
Nb+Ta0.150.45
Mechanical Properties
ConditionTensile Strength (MPa)Yield Strength 0.2% Proof (MPa)Elongation (% in 50mm)Hardness Rockwell C (HRC)
Solution Treated1105 typ1000 typ15 typ38 max
Condition 9001310 min1170 min10 min40 min
Condition 1150930 min724 min16 min28 min
Physical Properties
PropertyValue
Density7750 kg/m³
Mean Co-eff of Thermal Expansion (0-100°C)10.8 µm/m/°C
Thermal Conductivity (at 100°C)18.4 W/m·K
Specific Heat (0-100°C)460 J/kg·K
Electrical Resistivity800 nΩ·m
Alternative Grade Comparison
Alternative GradeReason for Choosing 17-4PH
431431 has higher toughness but 17-4PH offers better strength
416416 is free-machining but 17-4PH provides superior strength
316316 has higher corrosion resistance but much lower strength
22052205 has better corrosion resistance with lower strength
Heat Treatment
Solution treatment (Condition A): Heated at 1040°C for 0.5 h, then air-cooled to 30°C. Small sections can be oil quenched.
Age Hardening Conditions
ConditionHardening Temp (°C)Time (h)Typical Hardness (HRC)Tensile Strength (MPa)
AAnn-361100
H900482144-
H9254964421170-1320
H10255524381070-1220
H10755804361000-1150
H1100593435970-1120
H1150621433930-1080
Processing Characteristics
Welding: Can be welded using all conventional methods without pre-heating. Care should be taken to prevent weldment stresses.
Machining: Can be machined in solution-treated condition with machining rates similar to grade 304 steels.
Product Applications
  • Engine components
  • High strength and boat propeller shafts
  • Plastic moulding dies
  • Valves and gears
Product Images
Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening 0 Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening 1 Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening 2 Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening 3 Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening 4
Contact Us
Bright Polished 17-4PH Stainless Steel Round Bar with OD 3-300mm and Precipitation Hardening 5
Etichette:

17-4PH Alloy Stainless Steel Round Bar

Hot Rolled Stainless Steel Round Bar

Bright Surface Stainless Steel Round Bar