JIS G4312-2019 SUS436L Cold Rolled Stainless Steel Coil with Polished Surface and 0.3-3mm Thickness
Product Details
| Model Number | 436L | Shape | Flat |
|---|---|---|---|
| Technique | Cold Rolled | Surface Treatment | Polished |
| Thickness | 0.3-3mm | Carbon Content | ≤ 0.12 |
| Manganese Content | ≤1.00 | Silicon Content | ≤1.00 |
| Chromium Content | 16.0~18.0 | Molybdenum Content | 0.75~1.25 |
| Tensile Strength | 531 MPa Min | Yield Strength | 365 MPa Min |
| Elongation | 22% Min | Hardness | HRB 89 Max |
| Production Capacity | 50000kgs | ||
| Highlight | Cold Rolled Stainless Steel Coil,Polished Surface Stainless Steel Strip,0.3-3mm Thickness 436L Stainless Steel |
||
Product Description
JIS G4312-2019 SUS436L Cold Rolled Stainless Steel Coil 436L Strip
436 stainless steel is a modified steel grade of 434 that reduces the tendency to "wrinkle" during relatively stringent stretch forming operations. 430 is used as a molded product for automotive interior trim panels, and uses 434 and 436 stainless steel when better corrosion resistance is required.
436 Stainless Steel Specifications
- Standard: AISI, ASTM
- Model Number: 436
- UNS number: S43600
Chemical Composition
Carbon C: ≤ 0.12
Manganese Mn: ≤1.00
Silicon Si: ≤1.00
Chromium Cr: 16.0~18.0
Nickel Ni2: -
Phosphorus P: ≤0.04
Sulfur S: ≤0.03
Molybdenum Mo: 0.75~1.25
Nb: (5C~0.80)
Manganese Mn: ≤1.00
Silicon Si: ≤1.00
Chromium Cr: 16.0~18.0
Nickel Ni2: -
Phosphorus P: ≤0.04
Sulfur S: ≤0.03
Molybdenum Mo: 0.75~1.25
Nb: (5C~0.80)
Mechanical Properties at Room Temperature (Annealed)
Ultimate Tensile Strength: 77 KSI min (531 MPa min)
Yield Strength: (0.2% Offset) 53 KSI min (365 MPa min)
Elongation: 22% min
Hardness: HRB 89 max
Yield Strength: (0.2% Offset) 53 KSI min (365 MPa min)
Elongation: 22% min
Hardness: HRB 89 max
Available Stainless Steel Products
Grades
201, 301, 304, 304L, 309S, 310S, 316L, 317L, 321, 409L, 410, 410S, 430, 439, 444, 904L, 2205, 2507, etc.
Finishes
NO.1, 2B, 2D, BA, NO.4, NO.8, 8K, mirror, hair line, sand blast, brush, etching, checkered, embossed, etc.
Dimensions
Thickness: 0.2 - 200 mm
Width: 4 - 2000 mm
Length: 500 - 12000 mm / coil
Width: 4 - 2000 mm
Length: 500 - 12000 mm / coil
Stainless Steel Chemical Composition & Mechanical Properties
| Grade | C | Si | Mn | P | S | Ni | Cr | Mo | Hardness |
|---|---|---|---|---|---|---|---|---|---|
| 201 | ≤0.15 | ≤1.00 | 5.5/7.5 | ≤0.060 | ≤0.03 | 3.5/5.5 | 16.0/18.0 | - | HB≤241,HRB≤100,HV≤240 |
| 304 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.0/11.0 | 18.0/20.0 | - | HB≤187,HRB≤90,HV≤200 |
| 316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00/14.00 | 16.0/18.0 | 2.00/3.00 | HB≤187,HRB≤90,HV≤200 |
| 316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00/14.00 | 16.0/18.0 | 2.00/3.00 | HB≤187,HRB≤90,HV≤200 |
| 410 | ≤0.15 | ≤1.00 | ≤1.25 | ≤0.060 | ≤0.03 | ≤0.06 | 11.5/13.5 | - | HB≤183,HRB≤88,HV≤200 |
| 430 | ≤0.12 | ≤1.00 | ≤1.25 | ≤0.040 | ≤0.03 | - | 16.0/18.0 | - | HB≤183,HRB≤88,HV≤200 |