Incoloy 800H Round Bar Heat-Resistant Nickel Alloy Rod with Corrosion Resistance and Custom Cutting Any Length

証明	ISO, ASTM, GB, EN, DIN
最小注文数量	10kg
価格	US $35 / kg

商品の詳細

型番	800h	形	ラウンド
技術	熱間圧延	表面処理	ピクルスにすること
その他のグレード	800、800ht	長さ	任意の長さのカスタムカット
直径範囲	4-300mm	厚さの範囲	1.0-100mm
幅の範囲	1-1500mm	角棒のサイズ	44-100100mm
密度	8.0 g/cm3	融解範囲	1350-1400°C
抗張力	450MPa	降伏強さ	180MPa
伸長	35％
ハイライト	Heat-Resistant Incoloy 800H Round Bar , Corrosion Resistant Nickel Alloy Rod , Custom Cutting Any Length Heat-Resistant Alloy Bar

メッセージ

製品の説明

Incoloy 800H Round Bar Heat-Resistant Alloy Rod

High-performance iron-nickel-chromium alloy designed for extreme temperature and corrosive environments in furnace parts and chemical processing applications.

Product Specifications

Standards & Grades

Standard	AISI, ASTM, BS, DIN, GB, JIS
Grade	Monel series: 400 K500 Inconel series: 600 601 625 718 725 Incoloy series: 800 800H 825 925 Hastelloy series: B,B2,B3,C,C-276,C-4,C-22 Pure: Ni200, Ni201

Dimensions & Forms

Product Form	Size Range
Round Bar	Diameter: 4~300mm
Flat Bar	Thickness: 1.0~100mm Width: 1~1500mm
Square Bar	Size: 44-100100mm
Length	2m, 5.8m, 6m, or as required

Additional Specifications

Surface Finish	Black, peeled, polishing, bright, sand blast, hair line, etc.
Price Term	Ex-work, FOB, CFR, CIF, etc.
Delivery Time	Standard size is in stock, prompt delivery or as order's quantity

Material Characteristics

Chemical Composition

Element	Content (%)	Element	Content (%)
Nickel	30.0-35.0	Chromium	19.0-23.0
Iron	37.0-47.0	Carbon	0.05-0.10
Manganese	≤1.50	Silicon	≤1.00
Sulfur	≤0.015	Copper	≤0.75
Aluminum	0.15-0.60	Titanium	0.15-0.60
Phosphorus	≤0.030

Physical & Mechanical Properties

Property	Value	Condition
Density	8.0 g/cm³	Room Temperature
Melting Range	1350-1400°C	-
Tensile Strength	450 MPa	Solution Annealed
Yield Strength	180 MPa	Solution Annealed
Elongation	35%	Solution Annealed
Specific Heat Capacity	455 J/(kg*°C)	Room Temperature

Corrosion Resistance

Oxidizing Environments: Exceptional resistance to oxidizing salts and strongly oxidizing media
High-Temperature Gases: Excellent resistance to oxidation, carburization, and sulfidation
Aqueous Corrosion: Good resistance to stress corrosion cracking in chloride-containing environments
Organic Acids: Suitable for handling formic, acetic, and other organic acids

Applications

Chemical Processing Industry: Reactor components, heat exchanger tubes, baffles, and support structures
Heat Treatment & Industrial Furnaces: Radiant tubes, muffles, retorts, and heat treatment fixtures
Power Generation: Superheater and reheater tubes, header assemblies, and outlet piping
Petrochemical Industry: Ethylene production facilities and hydrocarbon processing equipment

Processing Guidelines

Heat Treatment

Process	Temperature Range	Duration	Cooling Method
Annealing	2100-2200°F (1150-1205°C)	30-60 minutes	Rapid Air or Water Quench
Stress Relief	1000-1600°F (540-870°C)	1 hour/inch thickness	Air Cool
Solution Treatment	2050-2150°F (1120-1175°C)	30-60 minutes	Rapid Cool