All Products
-
Stainless Steel Strip
-
Stainless Steel Sheet
-
Stainless Steel Plate
-
Stainless Steel Pipe
-
Stainless Steel Bar
-
Galvanized Steel Coil
-
Steel Plate
-
Steel Round Bar
-
Nickel Alloy
-
Seamless Steel Pipe
-
Stainless Steel Beam
-
Copper Plate Sheet
-
Copper Round Bar
-
stainless steel round bar
-
stainless steel channel bar
-
stainless steel angle bar
-
stainless steel coil strip
-
stainless steel flat bar
-
stainless steel circle
-
Pipe Fitting
-
Water Ripple Stainless Steel Sheet
-
Nickel Alloy and Super Alloy
-
cold rolled steel coil
-
copper
-
Nickel Base Alloy Products
-
Others
-
Raian IonescuMaterial quality very good. we have cooperate more than 10 Years. They trade lots kinds of steel material. All material quality good. They duty for all material quality. We are planing continue cooperate with them in the future
DIN1.4404 SUS316L Hot Rolled Polished Stainless Steel Plate Width 1000-2000mm Austenitic Grade
Product Details
| Model NO. | 316L | Shape | Round |
|---|---|---|---|
| Technique | Hot Rolled | Surface Treatment | Polished |
| Specification | 1220*2440, 1500*3000, 1500*6000, 2000*6000mm | Thickness | Cold Rolled 0.4 - 5.0mm, Hot Rolled 3.0 - 80.0mm |
| Standard Size | Cold Rolled 1000*2000mm 1219*2438mm 1500*3000mm, Hot Rolled 1500*6000mm 1800*6000mm 2000*60000mm | Carbon Content | 0.03% Max |
| Manganese Content | 2.0% Max | Chromium Content | 16.0-18.0% |
| Molybdenum Content | 2.00-3.00% | Nickel Content | 10.0-14.0% |
| Tensile Strength | 485 MPa Min | Yield Strength | 170 MPa Min |
| Elongation | 40% Min | ||
| Highlight | Hot Rolled Stainless Steel Plate,Polished Stainless Steel Plate,Width 1000-2000mm Stainless Steel Plate |
||
Product Description
DIN1.4404 SUS316L Stainless Steel Plates
Width 1000-2000mm Alloy 316/316L Austenitic Stainless Steel Plate
Product Specifications
| Products Name | 316L Stainless Steel Plate |
|---|---|
| Standard | ASTM JIS GB EN DIN |
| Thickness | Cold Rolled: 0.4 - 5.0mm, Hot Rolled: 3.0 - 80.0mm |
| Standard Size | Cold Rolled: 1000×2000mm, 1219×2438mm, 1500×3000mm Hot Rolled: 1500×6000mm, 1800×6000mm, 2000×6000mm |
| Brand | POSCO, TISCO, BAOSTEEL, JISCO |
| Other Grades | 201, 304, 309, 310, 317L, 321, 347, 410, 420, 430, 431, 441, 445, 630, 631, 2205, 2507, 904L, 254SMO, S31254, 253MA, etc. |
| Service | Cutting |
Grade 316L is the low carbon version of 316 stainless steel and is immune from sensitization (grain boundary carbide precipitation). This makes it extensively used in heavy gauge welded components (over about 6mm). There is commonly no appreciable price difference between 316 and 316L stainless steel.
The austenitic structure gives these grades excellent toughness, even down to cryogenic temperatures. Compared to chromium-nickel austenitic stainless steels, 316L stainless steel offers higher creep, stress to rupture and tensile strength at elevated temperatures.
Chemical Composition of 316L Stainless Steel
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N |
|---|---|---|---|---|---|---|---|---|---|
| 316L | Min: - Max: 0.03 |
Min: - Max: 2.0 |
Min: - Max: 0.75 |
Min: - Max: 0.045 |
Min: - Max: 0.03 |
Min: 16.0 Max: 18.0 |
Min: 2.00 Max: 3.00 |
Min: 10.0 Max: 14.0 |
Min: - Max: 0.10 |
Mechanical Properties of 316L Stainless Steel
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50 mm) min | Hardness HB (Max) |
|---|---|---|---|---|
| 316L | 485 | 170 | 40 | 217 |
Corrosion Resistance
Excellent in a range of atmospheric environments and many corrosive media - generally more resistant than 304. Subject to pitting and crevice corrosion in warm chloride environments, and to stress corrosion cracking above about 60°C. Considered resistant to potable water with up to about 1000 mg/L chlorides at ambient temperatures, reducing to about 500 mg/L at 60°C.
316 is usually regarded as the standard "marine grade stainless steel", but it is not resistant to warm seawater. In many marine environments, 316 does exhibit surface corrosion, usually visible as brown staining. This is particularly associated with crevices and rough surface finish.
Heat Resistance
Good oxidation resistance in intermittent service to 870°C and in continuous service to 925°C. Continuous use of 316 in the 425-860°C range is not recommended if subsequent aqueous corrosion resistance is important. Grade 316L is more resistant to carbide precipitation and can be used in the above temperature range. Grade 316H has higher strength at elevated temperatures and is sometimes used for structural and pressure-containing applications at temperatures above about 500°C.
Heat Treatment
Solution Treatment (Annealing) - Heat to 1010-1120°C and cool rapidly. These grades cannot be hardened by thermal treatment.
Machining
316L stainless steel tends to work harden if machined too quickly. For this reason, low speeds and constant feed rates are recommended. 316L stainless steel is also easier to machine compared to 316 stainless steel due to its lower carbon content.
Hot and Cold Working
316L stainless steel can be hot worked using the most common hot working techniques. Optimal hot working temperatures should be in the range 1150-1260°C, and certainly should not be less than 930°C. Post-work annealing should be carried out to induce maximum corrosion resistance.
Most common cold working operations such as shearing, drawing, and stamping can be performed on 316L stainless steel. Post-work annealing should be carried out to remove internal stresses.
Applications
- Food preparation equipment particularly in chloride environments
- Pharmaceuticals
- Marine applications
- Architectural applications
- Medical implants, including pins, screws and orthopedic implants like total hip and knee replacements
- Fasteners
Product Images
About Our Company
Our company is a professional agent of many stainless steel plants at home and abroad for all kinds of stainless steel plate. In the stainless steel industry, we enjoy great popularity and have industry influence as a premier agent, especially in special stainless steel distribution and import/export trade.
We represent TISCO, POSCO, ESS, BAOSTEEL, JISCO, FUXIN, LISCO, HONGWANG, and are special dealers in China for ACERINOX, OUTOKUMPU, Thyssen Krupp, APERAM, NISSHIN, NSSC, Nippon Yakin Kogyo and other well-known foreign steel mills.
Our main product lines include 304 Series (304, 304L, 304H, 304N), 316 series (S31603, 022Cr17Ni12Mo2, 316L, 316Ti, 316H, 317L, etc.), 321 series (S32168, 06Cr18Ni1611Ti, 321, 321H, etc.), 310S, 309S, 1Cr25Ni20SI2, 1Cr20Ni14SI2, 253MA and other heat resistant stainless steel, 2205, 2304, 2101, 2507 and other duplex stainless steel.