Nickel Based Anti Oxidation Hot Rolled Inconel 600 Stainless Steel Plate
Product Details
| Model Number | Inconel 600 | Shape | Flat |
|---|---|---|---|
| Technique | Hot Rolled | Surface Treatment | Polished |
| Specification | 1220*2440, 1500*3000, 1500*6000, 2000*6000mm | Nickel Content | 72.0-76.0% |
| Chromium Content | 14.0-17.0% | Iron Content | 6.0-10.0% |
| Carbon Content | Max 0.15% | Manganese Content | Max 1.0% |
| Silicon Content | Max 0.5% | Sulfur Content | Max 0.015% |
| Ultimate Tensile | 760 MPa | Yield Strength | 585 MPa |
| Elongation | 10% | ||
| Highlight | Nickel Based Inconel 600 Plate,Anti Oxidation Nickel Alloy Plate,Hot Rolled Stainless Steel Plate |
||
Product Description
Inconel 600 (UNS N06600) Nickel-Chromium Alloy
Inconel 600 is a high-performance nickel-chromium alloy designed for use from cryogenic to elevated temperatures up to 2000°F (1093°C). This alloy offers excellent oxidation resistance, high strength, and superior corrosion resistance in various industrial environments.
Chemical Composition
Ni 72.0%, Cr 15.5%, Fe 8.0%, Mn 1.0%, C 0.15%, Cu 0.5%, Si 0.5%, S 0.015%
Available Forms
Bar, wire cuts, sheet, plate, strip, tube, and pipe
Key Characteristics
- Excellent oxidation resistance at high temperatures
- Superior resistance to chloride-ion stress-corrosion cracking
- Good performance in carburizing and chloride-containing environments
- Resistant to alkaline solutions and sulfur compounds
- Non-magnetic with excellent mechanical properties
- Good workability and readily weldable
- High strength combined with good formability
Chemical Requirements
| Element | Min (%) | Max (%) |
|---|---|---|
| Ni | 72.0 | - |
| C | - | 0.15 |
| Mn | - | 1.0 |
| Cr | 14.0 | 17.0 |
| S | - | 0.015 |
| Si | - | 0.5 |
| Fe | 6.0 | 10.0 |
Mechanical Properties
| Condition | Ultimate Tensile | Yield Strength (0.2% OS) | Elongation (%) |
|---|---|---|---|
| Cold Worked | 110 KSi (760 MPa) min | 85 KSi (585 MPa) min | 10 min |
| Hot Worked | 90 KSi (620 MPa) min | 40 KSi (275 MPa) min | 25 min |
Industry Applications
- Thermocouple sheaths
- Ethylene dichloride (EDC) cracking tubes
- Chemical and food processing equipment
- Heat treating fixtures and furnace components
- Nuclear reactor components
- Vinyl chloride monomer production
- Caustic alkali production equipment
- Chlorinated and fluorinated hydrocarbon processing
Specifications
| Form | Standard |
|---|---|
| Metal Type | UNS N06600 |
| Bar | ASTM B166, AMS 5665, Din 17752 |
| Sheet/Plate | ASTM B168, AMS 5540, Din 17750 |
| Tube/Pipe | ASTM B167 |
| Forging | ASTM B564, Din 17754 |
| Weld Wire | FM 82/ ERNiCr-3 |
| Weld Electrode | FM 182/ ENiCrFe-3 |
| DIN | 2.4816 |
Machining Guidelines
Carbide tools are recommended for optimal machining performance. Starting rates typically achieve better than 50% of Type 304 stainless steel performance.
INCONEL® is a registered trademark. Sheet and plate are typically supplied in annealed condition. Bar stock may require stress relief or annealing before heading operations.