Hot Rolled ASTM A240 410 Stainless Steel Plate SS 410 Plate 1Cr13 Stainless Steel Plate

Certification	ASTM, GB, DIN
Minimum Order Quantity	50 kg
Price	US $1.35-2.65 / kg

Product Details

Model NO.	410	Shape	Flat
Technique	Hot Rolled	Surface Treatment	Polished
Specification	12202440, 15003000, 15006000, 20006000mm	Carbon Content	0.15 Max
Manganese Content	1.00 Max	Silicon Content	1.00 Max
Chromium Content	11.50 - 13.50	Nickel Content	0.75 Max
Sulfur Content	0.03 Max	Phosphorus Content	0.04 Max
Density	0.276 Lb/in3	Melting Range	2700-2790°F (1482-1532°C)
Modulus Of Elasticity	29 X 106 Psi (200 GPa)
Highlight	Hot Rolled Stainless Steel Plate , ASTM A240 SS 410 Plate , 410 Stainless Steel 1Cr13 Plate

Leave a Message

Product Description

Hot Rolled ASTM A240 410 Stainless Steel Plate

Type 410 stainless steel is a hardenable, martensitic stainless steel that combines superior wear resistance with excellent corrosion resistance. This grade offers high strength, heat resistance, good ductility, and maintains magnetic properties in both annealed and hardened conditions.

Material Properties

410 stainless steel provides good corrosion resistance in mild atmospheres, steam, and mild chemical environments, making it well-suited for highly stressed components across various industries.

Standard Specifications

UNS S41000, AMS 5504, AMS 5613 (Chemistry only), ASTM A240, ASTM A276, ASTM A493, ASTM F899, ASME SA240, B50991B

Chemical Composition

Element	Percent by Weight
Carbon (C)	0.15 max
Manganese (Mn)	1.00 max
Silicon (Si)	1.00 max
Chromium (Cr)	11.50 - 13.50
Nickel (Ni)	0.75 max
Sulfur (S)	0.03 max
Phosphorus (P)	0.04 max

Physical Properties

Density: 0.276 lb/in³
Specific Gravity: 7.65
Melting Range: 2700-2790°F (1482-1532°C)
Modulus of Elasticity: 29 x 10⁶ psi (200 GPa)

Thermal Expansion Coefficient

Temperature Range	Coefficient
20-200°C (68-392°F)	10.5 x 10⁻⁶ cm/cm/°C (5.9 x 10⁻⁶ in/in/°F)
20-600°C (68-1112°F)	11.6 x 10⁻⁶ cm/cm/°C (6.5 x 10⁻⁶ in/in/°F)

Thermal Conductivity

Temperature	W/m·K	Btu/(hr·ft·°F)
100°C (212°F)	0.249	14.4

Specific Heat

0.11 Btu/lb·°F

Electrical Resistivity

Temperature	Resistivity (microhm-cm)
20°C (68°F)	56

Mechanical Properties

Property	Value
HRB (Annealed)	82-96
0.2% Offset Yield Strength	30-42 ksi (205-290 MPa)
Tensile Strength	65-74 ksi (450-510 MPa)
Elongation (2" / 51 mm)	20-34%
Hardening Response HRC	38-45