All Products
-
Stainless Steel Strip
-
Stainless Steel Sheet
-
Stainless Steel Plate
-
Stainless Steel Pipe
-
Stainless Steel Bar
-
Galvanized Steel Coil
-
Steel Plate
-
Steel Round Bar
-
Nickel Alloy
-
Seamless Steel Pipe
-
Stainless Steel Beam
-
Copper Plate Sheet
-
Copper Round Bar
-
stainless steel round bar
-
stainless steel channel bar
-
stainless steel angle bar
-
stainless steel coil strip
-
stainless steel flat bar
-
stainless steel circle
-
Pipe Fitting
-
Water Ripple Stainless Steel Sheet
-
Nickel Alloy and Super Alloy
-
cold rolled steel coil
-
copper
-
Nickel Base Alloy Products
-
Others
-
Raian IonescuMaterial quality very good. we have cooperate more than 10 Years. They trade lots kinds of steel material. All material quality good. They duty for all material quality. We are planing continue cooperate with them in the future
S32101 Duplex Stainless Steel Plate - Corrosion Resistant, High Strength, and Good Weldability
Product Details
| Model NO. | S32101 | Shape | Flat |
|---|---|---|---|
| Technique | Hot Rolled | Surface Treatment | Pickling |
| Specification | 1220*2440, 1500*3000, 1500*6000, 2000*6000mm | Production Capacity | 50000kgs |
| Yield Strength | ≥ 530 MPa (PLATE CR), ≥ 450 MPa (PLATE HR/QUARTO) | Tensile Strength | ≥ 700 MPa (PLATE CR), ≥ 650 MPa (PLATE HR/QUARTO) |
| Elongation | ≥ 30% | Hardness | ≤ 290 HB (PLATE HR/QUARTO) |
| Impact Resistance | ≥ 50 J (PLATE CR/HR), ≥ 27 J (PLATE QUARTO) | Heat Treatment | 1020 - 1100°C Solution Annealing |
| Max Temperature | 250 °C | Chromium Content | Balanced (part Of Duplex Chemistry) |
| Nitrogen Content | Balanced (part Of Duplex Chemistry) | ||
| Highlight | Corrosion Resistant Stainless Steel Plate,High Strength Duplex Steel Plate,Good Weldability S32101 Plate |
||
Product Description
S32101 Stainless Steel Plate / LDX 2101 Duplex Steel Plate
Material Description
LDX 2101 is a low nickel-alloyed duplex stainless steel with balanced chemistry of chromium, molybdenum, and nitrogen content to achieve excellent resistance to localized and uniform corrosion. The duplex microstructure contributes to high strength and superior resistance to stress corrosion cracking. Duplex steels offer good weldability. Due to risk of embrittlement, LDX 2101 should not be used at temperatures above 250°C. This alloy provides very price-stable high strength performance.
Applications
The main applications are for components requiring corrosion resistance superior to 304L stainless steel.
LDX 2101 Key Characteristics
- Ideal for tank production where corrosion strength requirements are sufficient
- Excellent resistance to stress corrosion cracking
- Superior resistance to general corrosion
- High mechanical strength properties
- Exceptional resistance to erosion corrosion and corrosion fatigue
Heat Treatment
Solution annealing at 1020-1100°C followed by water quenching.
Weldability
Very good welding characteristics
Chemical Composition & Standards
Product Standards: EN 10088-2, EN 10088-4, ASTM A240, EN ISO 9445-2
Approvals: NACE MR0175/ISO 15156-3:2015, PED 97/23/EC, CPR 305/2011/EU
Approvals: NACE MR0175/ISO 15156-3:2015, PED 97/23/EC, CPR 305/2011/EU
Mechanical Properties
| Product Form | Yield Strength Rp0.2 (MPa) | Tensile Strength Rm (MPa) | Elongation (%) | Hardness (HB) | Impact, Charpy-V, -40°C (J) |
|---|---|---|---|---|---|
| Plate CR (Coil) | ≥ 530 | ≥ 700 | ≥ 30 | - | ≥ 50 |
| Plate HR (Coil) | ≥ 450 | ≥ 650 | ≥ 30 | ≤ 290 | ≥ 50 |
| Plate (Quarto) | ≥ 450 | ≥ 650 | ≥ 30 | ≤ 290 | ≥ 27 |