304 Stainless Steel Perforated Sheet with 0.1-10mm Hole Cold Rolled for Durability

証明	ISO, AISI, ASTM
最小注文数量	50 kg
価格	US $2.15-2.55 / kg

商品の詳細

モデル番号	304 316L 904L 310S	形	フラット
技術	冷間圧延	表面処理	明るい
クロムの内容	18%	ニッケル含有量	8%
仕様	12202440,15003000,15006000,20006000mm	抗張力	≥ 520 MPa
降伏強さ	≧205MPa	伸長	40％以上
硬度	≤ 187HB; ≤ 90HRB; ≤ 200HV	融点	1398～1454℃
熱伝導率	16.3～21.5W/mK	比熱容量	0.50KJ/kgK
抵抗率	0.73Ω・m
ハイライト	304 Stainless Steel Perforated Sheet , Cold Rolled Perforated Sheet , 0.1-10mm Hole Stainless Steel Sheet

メッセージ

製品の説明

Stainless Steel Perforated Sheets

High-quality perforated sheets available in 304, 316L, 904L, and 310S stainless steel grades with hole sizes ranging from 0.1mm to 10mm.

Surface Treatments & Characteristics

Surface Finish	Characteristics and Applications
NO.2B	Superior brightness and flatness compared to NO.2D. Enhanced mechanical properties through special surface treatment, suitable for comprehensive applications.
NO.1	Heat treatment and pickling finish after hot rolling process.
NO.4	Polished with #150-#180 grit abrasive belt. Features better brightness with discontinuous coarse striations. Used for bathtubs, building ornaments, appliances, kitchen utensils, and food processing equipment.
HL	Polished with #150-#320 grit abrasive belt on NO.4 finish. Continuous streaks pattern. Ideal for building ornaments, elevators, doors, and frontal plates.
BA	Cold rolled, bright annealed, and skin-passed. Excellent mirror-like brightness and reflectivity. Suitable for kitchen apparatus and decorative applications.
8K	Exceptional brightness and superior mirror-like reflectivity.

Chemical Composition

Carbon (C): ≤0.08% | Silicon (Si): ≤1.0% | Manganese (Mn): ≤2.0%
Chromium (Cr): 18.0-20.0% | Nickel (Ni): 8.0-10.0%
Sulfur (S): ≤0.03% | Phosphorus (P): ≤0.045%

Physical Properties

Property	Value
Tensile Strength (MPa)	≥ 520
Yield Strength (MPa)	≥ 205
Elongation (%)	≥ 40
Section Shrinkage (%)	≥ 60
Hardness	≤ 187HB; ≤ 90HRB; ≤ 200HV
Melting Point (°C)	1398 - 1454
Specific Heat Capacity (0-100°C, KJ/kgK)	0.50
Thermal Conductivity (W/m·K)	16.3 (100°C), 21.5 (500°C)
Linear Expansion Coefficient	17.2 (0-100°C), 18.4 (0-500°C)
Resistivity (20°C, 10⁻⁶ Ω·m)	0.73
Longitudinal Elastic Modulus (20°C, KN/mm²)	193

Corrosion Resistance

Stainless steel offers excellent resistance to corrosion and staining, requires low maintenance, and maintains its attractive luster, making it ideal for numerous applications. This alloy is widely used in cookware, cutlery, household hardware, surgical instruments, major appliances, industrial equipment, and automotive and construction materials for large buildings. It is particularly suitable for commercial kitchens and food processing plants as it can be steam-cleaned and sterilized without requiring paint or other surface finishes.