Tisco 321 Stainless Steel Plate and Sheet with 1800mm 2000mm Width and 3.0 - 14.0mm Thickness

Certification	RoHS, AISI, ASTM, GB, DIN, JIS
Minimum Order Quantity	50 kg
Price	US $2.75-3.21 / kg

Product Details

Model NO.	321	Shape	Flat
Technique	Cold Rolled	Surface Treatment	Bright
Specification	12202440, 15003000, 15006000, 20006000mm	Production Capacity	50000kgs
Thickness	0.6 To 80 Mm	Width	1219mm, 1500mm, 1800mm, 2000mm
Length	2m, 2.44m, 3m, 6m	Finish	SATIN, 2B, 2D, BA NO (8), CR, HR, No.1, 1D, No.4, BA, 8K, Hairline, Brush, Mirror
Carbon Content	0.08	Chromium Content	17.0-19.0
Nickel Content	9.0-12.0	Yield Strength	30 Ksi
Tensile Strength	75 Ksi
Highlight	321 Stainless Steel Plate , 1800mm 2000mm Width Stainless Steel Sheet , 3.0 - 14.0mm Thickness Stainless Steel Plate

Leave a Message

Product Description

TISCO 321 Stainless Steel Plate

Available in 1800mm and 2000mm widths with thickness ranging from 3.0mm to 14.0mm

Product Specifications

Product Type	321 Stainless Steel Sheet, 321 Stainless Steel Plate
Specification	ASTM A240 / ASME SA240
Dimensions	Cold rolled: 4ft8ft [12192438mm] Hot rolled: 5ft20ft, 6ft20ft [15006000mm 18006000mm 2000*6000mm]
Thickness	0.6 to 80 mm
Width	1219mm, 1500mm, 1800mm, 2000mm
Length	2m, 2.44m, 3m, 6m or as required
Finish	Satin, 2B, 2D, BA NO (8), Cold rolled sheet (CR), Hot rolled plate (HR), No.1 finish hot rolled, 1D, No.4, BA, 8K, hairline, brush, mirror, etc.
Our Services	Laser Cutting, bending, welding, polishing
Forms / Shapes	Plate, Sheet, Coils, Foils, Strip, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate

Alternative Trade Names

SS 321, SUS 321, Inox 321, DIN 1.4541, UNS S32100, AISI 321, SAE 321 Sheet

Available Grades

201, 202, 304, 304L, 304H, 309S, 310S, 310H, 310Si2, 316L, 316Ti, 316LN, 317L, 321, 347, 409L, 410, 410S, 416, 420, 430, 431, 436L, 439, 441, 443, 444, S31803, S32750, 904L, S30815, S31254, C276, C4, 600, 625, etc.

Grade 321 / 321H Stainless Steel Overview

321 stainless steel is a titanium stabilized grade designed for service in the 1000-1600°F temperature range. For optimal performance at temperatures up to 1600°F, a stabilizing treatment at 1550-1650°F with air cooling is recommended to provide maximum resistance to intergranular corrosion and polythionic acid stress corrosion cracking.

This grade is readily weldable using all common methods, including submerged arc welding. Recommended weld fillers include AWS ER347 bare wire and E347 covered electrodes. With a machinability rating of 45% relative to AISI B1112, 321 stainless steel offers similar machining characteristics to 304 stainless steel.

Available Forms: Sheet, plate, coil, strip, wire, pipe, tube, bar, profile, round, flat, square, hexagonal

Specifications and Certifications

Grade 321/321H
ASTM A240, ASME SA240, BS EN 10028-7, BS EN 10088-2 and BS EN 10088-4
EN 10088/2, EN 10088/4 and CE Marking
NACE MR 0175/ISO 15156 Certification

Applications

Aircraft piston engine manifolds
Expansion joints
Firearms production
Thermal oxidizers
Refinery equipment
High temperature chemical process equipment

Chemical Composition

Element	321
Carbon	0.08
Chromium	17.0-19.0
Nickel	9.0-12.0
Manganese	2.00
Silicon	0.75
Nitrogen	0.10
Phosphorus	0.045
Sulfur	0.030
Titanium	5(C+N) min / 0.70 max

* Maximum, unless range is indicated

Mechanical Properties

Property	321
Yield Strength, min. (ksi)	30
Tensile Strength, min. (ksi)	75
Elongation, min. (%)	40
Hardness, max. (Rb)	95

Grade Specification Comparison

Grade	UNS No	Old British	Euronorm	Swedish SS	Japanese JIS
321	S32100	321S31	1.4541	2337	SUS 321
321H	S32109	321S51	1.4878	-	SUS 321H
347	S34700	347S31	1.4550	2338	SUS 347

Alternative Grades

Grade	Why it might be chosen instead of 321
304L	The requirement is for resistance to intergranular corrosion, not for high-temperature strength
3CR12	Only a mild "high temperature" environment is present… up to about 600°C
304H	Only a mild "high temperature" environment is present… up to about 800°C
310	The temperature of the operating environment is up to about 1100°C - too high for 321 or 321H
S30815 (253MA)	The temperature of the operating environment is up to about 1150°C - too high for 321 or 321H