ASTM B409 Incoloy 800H Round Bar Precision-Machined Nickel Alloy Rod for Petrochemical & Power Sectors

인증	ISO, ASTM
최소 주문 수량	50kg

제품 상세 정보

모델 번호.	800H	모양	둥근
기술	열간압연	표면 처리	산세
길이	6m 이내에	프로세스	연마, 열처리
사양	5-300mm	밀도	80.0g/cm3
용융 범위	1350-1400' Ｃ	인장강도	≥450N/mm²
항복 강도	≥180N/mm²	연장	≥35%
브리넬 경도	≤210	고온 인장	≥450 MPa
고온 수율	≥170MPa
강조하다	ASTM B409 Incoloy 800H Round Bar , Precision-Machined Nickel Alloy Rod , Petrochemical & Power Sectors Alloy Bar

메시지를 남겨주세요

제품 설명

ASTM B409 Incoloy 800H Round Bar Precision-Machined Alloy Rod

Designed for petrochemical and power generation sectors, this precision-machined nickel-iron-chromium alloy rod delivers unmatched stability and durability in extreme industrial environments.

Product Specifications

Standard	AISI, ASTM, BS, DIN, GB, JIS
Grade	Monel series: 400 K500 Inconel series: 600 601 625 718 725 Incoloy series: 800 800H 825 925 Hastelloy series: B,B2,B3,C,C-276,C-4,C-22 Pure: Ni200, Ni201
Specifications	Round bar: Diameter: 4~300mm Flat bar: Thickness: 1.0~100mm, Width: 1~1500mm Square bar: Size: 44-100100mm Length: 2m, 5.8m, 6m, or as required Surface: Black, peeled, polishing, bright, sand blast, hair line, etc.
Price Term	Ex-work, FOB, CFR, CIF, etc.
Delivery Time	Standard size is in stock, prompt delivery or as order's quantity

Material Characteristics

Incoloy 800H (UNS N08810, W. Nr. 1.4958) features a face-centered cubic lattice structure optimized through precise chemical composition control and specialized heat treatment. Its unique formulation balances nickel, chromium, and iron with trace elements to achieve superior performance metrics.

Physical & Mechanical Properties (ASTM B409 Compliance)

Property Category	Specific Parameter	Value
Physical Properties	Density	8.0 g/cm³ (0.287 lb/in³)
Physical Properties	Melting Range	1350-1400°C (2475-2525°F)
Room Temperature Mechanics	Tensile Strength (Rm)	≥450 N/mm² (65 ksi)
	Yield Strength (Rp0.2)	≥180 N/mm² (26 ksi)
	Elongation (A5%)	≥35%
	Brinell Hardness (HB)	≤210
High-Temperature Mechanics (1400°F/760°C)	Tensile Strength	≥450 MPa (65 ksi)
	Yield Strength	≥170 MPa (25 ksi)
	10,000-Hour Creep Rupture Strength	7.3 ksi

Precision Machining Capabilities

Dimensional Accuracy: Diameter tolerances as tight as ±0.005mm and straightness within 0.02mm/m
Surface Finish: Precision grinding achieves Ra 0.8μm or better
Heat Treatment Optimization: Solution annealing at 1100°C+ with controlled cooling
Quality Validation: 100% dimensional inspection, ultrasonic testing, and chemical composition verification

Application Advantages

Petrochemical Industry
Ethylene cracking furnaces, hydrogenation reactors, and acid processing equipment with superior corrosion resistance

Power Generation
Nuclear power plants, fossil fuel plants, and renewable energy systems with high-temperature stability

Compliance & Quality Assurance

Our ASTM B409 Incoloy 800H round bars meet global industry standards including ASME SB-409, EN 10216-5, and DIN 17459. Each batch includes comprehensive mill test reports with chemical composition verification, mechanical properties, heat treatment records, and non-destructive testing results.

Key Benefits

ASTM B409 Compliance: Guaranteed adherence to stringent material and performance standards
Long-Term Cost Efficiency: Extended service life (typically 2-3x longer than 316 stainless steel)
Application Expertise: Technical support including welding guidance and heat treatment consultation
Customization: Available in diameters from 10mm to 200mm with specialized surface treatments

꼬리표:

ASTM B409 Incoloy 800H Round Bar Precision-Machined Nickel Alloy Rod for Petrochemical & Power Sectors

ASTM B409 Incoloy 800H Round Bar

Precision-Machined Nickel Alloy Rod

Petrochemical & Power Sectors Alloy Bar